Influence of metal-support interactions on reaction pathways over Ni/CeZrOx–Al2O3 catalysts for ethanol steam reforming

This work investigates selective Ni locations over Ni/CeZrO_x–Al₂O₃ catalysts at different Ni loading contents and their influences on reaction pathways in ethanol steam reforming (ESR). Depending on the Ni loading contents, the added Ni selectively interacts with CeZrO_x–Al₂O₃, resulting in the stepwise locations of Ni over CeZrO_x–Al₂O₃. This behavior induces a remarkable difference in hydrogen production and coke formation in ESR. The selective interaction between Ni and CeZrO_x for 10-wt.% Ni generates more oxygen vacancies in the CeZrO_x lattice. The Ni sites near the oxygen vacancies enhance reforming via steam activation, resulting in the highest hydrogen production rate of 1863.0 μmol/g_cat·min. In contrast, for 15 and 20-wt.% Ni, excessive Ni is additionally deposited on Al₂O₃ after the saturation of Ni–CeZrO_x interactions. These Ni sites on Al₂O₃ accelerate coking from the ethylene produced on the acidic sites, resulting in a high coke amount of 19.1 mg_c/g_cat·h (20Ni/CZ-Al).     

低压静电场辅助冷冻对竹笋品质的影响

为研究低压静电场辅助冷冻对竹笋冻结特性的影响，以冻结曲线、硬度、水分损失率、水分迁移、冰晶形态和组织微观结构为指标，探究低压静电场辅助冷冻（－35 ℃）和普通冷冻（－35 ℃）条件下竹笋品质的变化规律。结果表明：低压静电场辅助冷冻提高了冻结效率，改变了冰晶形态及分布，减轻了组织微观结构破损程度，改善了解冻汁液流失情况。与静电板间距10、20、30、40 cm处的冷冻竹笋解冻后水分损失率分别为14.16%、12.58%、9.73%、10.44%，显著低于对照组（21.01%）（P＜0.05），硬度分别为461.19、507.48、496.65 g和455.31 g，显著高于对照组（350.70 g）（P＜0.05）。低场核磁共振分析结果表明，在低压静电场辅助冷冻下竹笋解冻后汁液流失减少，扫描电子显微镜观察结果显示，竹笋纤维排列整齐，组织微观结构保持较好。低压静电场辅助冷冻可有效改善竹笋品质，可为利用低压静电场进行果蔬的冷冻贮藏和冷链运输提供参考。     

No-Reference Video Quality Assessment using novel hybrid features and two-stage hybrid regression for score level fusion

This paper presents a novel No-Reference Video Quality Assessment (NR-VQA) model that utilizes proposed 3D steerable wavelet transform-based Natural Video Statistics (NVS) features as well as human perceptual features. Additionally, we proposed a novel two-stage regression scheme that significantly improves the overall performance of quality estimation. In the first stage, transform-based NVS and human perceptual features are separately passed through the proposed hybrid regression scheme: Support Vector Regression (SVR) followed by Polynomial curve fitting. The two visual quality scores predicted from the first stage are then used as features for the similar second stage. This predicts the final quality scores of distorted videos by achieving score level fusion. Extensive experiments were conducted using five authentic and four synthetic distortion databases. Experimental results demonstrate that the proposed method outperforms other published state-of-the-art benchmark methods on synthetic distortion databases and is among the top performers on authentic distortion databases. The source code is available at https://github.com/anishVNIT/two-stage-vqa.     

Superradiant Emission from Coherent Excitons in van Der Waals Heterostructures

Recent advancements in isolation and stacking of layered van der Waals materials have created an unprecedented paradigm for demonstrating varieties of 2D quantum materials. Rationally designed van der Waals heterostructures composed of monolayer transition-metal dichalcogenides (TMDs) and few-layer hBN show several unique optoelectronic features driven by correlations. However, entangled superradiant excitonic species in such systems have not been observed before. In this report, it is demonstrated that strong suppression of phonon population at low temperature results in a formation of a coherent excitonic-dipoles ensemble in the heterostructure, and the collective oscillation of those dipoles stimulates a robust phase synchronized ultra-narrow band superradiant emission even at extremely low pumping intensity. Such emitters are in high demand for a multitude of applications, including fundamental research on many-body correlations and other state-of-the-art technologies. This timely demonstration paves the way for further exploration of ultralow-threshold quantum-emitting devices with unmatched design freedom and spectral tunability.     

Preparation of high-activity coal char-based catalysts from high metals containing coal gangue and lignite for catalytic decomposition of biomass tar

The potential of using high metals containing coal gangue and lignite to prepare high-activity coal char-based catalysts is investigated for effective biomass tar decomposition. Loose structure and rough surface are formed for these char-based catalysts with heterogeneous distribution of a large number of inorganic particles. In the biomass tar decomposition, the performance of the coal char-based catalysts is significantly influenced by the content of the metals in the raw materials and coal gangue char (GC) with the ash content as high as 50.80% exhibits the highest activity in this work. A high biomass tar conversion efficiency of 93.5% is achieved at 800 °C along with a significant increase in the fuel gas product. During the five-time consecutive tests, the catalytic performance of GC increases a little at the second or third times reuse and remains relatively stable, showing the remarkable stability of the catalyst in biomass tar decomposition applications.     

Agronomic performance of high oleic,low linolenic soybean in Tennessee

Soybean oil hydrogenation alters the linolenic acid molecule to prevent the oil from becoming rancid, however, health reports have indicated trans-fat caused by hydrogenation, is not generally regarded as safe. Typical soybeans contain approximately 80 g kg⁻¹ to 120 g kg⁻¹ linolenic acid and 240 g kg⁻¹ of oleic acid. In an effort to accommodate the need for high-quality oil, the United Soybean Board introduced an industry standard for a high oleic acid greater than 750 g kg⁻¹ and linolenic acid less than 30 g kg⁻¹ oil. By combing mutations in the soybean plant at four loci, FAD2-1A and FAD2-1B, oleate desaturase genes and FAD3A and FAD3C, linoleate desaturase genes, and seed oil will not require hydrogenation to prevent oxidation and produce high-quality oil. In 2017 and 2018, a study comparing four near-isogenic lines across multiple Tennessee locations was performed to identify agronomic traits associated with mutations in FAD3A and FAD3C loci, while holding FAD2-1A and FAD2-1B constant in the mutant (high oleic) state. Soybean lines were assessed for yield and oil quality based on mutations at FAD2-1 and FAD3 loci. Variations of wild-type and mutant genotypes were compared at FAD3A and FAD3C loci. Analysis using a generalized linear mixed model in SAS 9.4, indicated no yield drag or other negative agronomic traits associated with the high oleic and low linolenic acid genotype. All four mutations of fad2-1A, fad2-1B, fad3A, and fad3C were determined as necessary to produce a soybean with the new industry standard (>750 g kg⁻¹ oleic and <30 g kg⁻¹ linolenic acid) in a maturity group-IV-Late cultivar for Tennessee growers.     

Phase composition,microstructure, and properties of Al4O4C–(Al2OC)1-x(AlN)x –Zr2Al3C4–Al2O3 refractories prepared at high temperatures in nitrogen

The novel Al₄O₄C–(Al₂OC)_1-x(AlN)_x–Zr₂Al₃C₄–Al₂O₃ refractories with ultra-low carbon content have been successfully prepared by constructing the core-shell structure of aluminum at 1300–1700°C in nitrogen. The phase composition, microstructure, and properties of the novel refractories are deeply investigated. The cracking temperature on the core-shell structure of aluminum is further explored and the reaction mechanism of Zr₂Al₃C₄ has also added explanation. The results show that the novel refractories have excellent physical properties and cannot be corroded by molten iron. There exist two different Al₂OC solid solutions in the novel refractories, Al₂OC-rich (Al₂OC)_1-x(AlN)_x and AlN-rich (Al₂OC)_1-x(AlN)_x. The temperatures affect their relative content. When temperatures are less than 1600°C, the relative content of Al₂OC-rich (Al₂OC)_1-x(AlN)_x is more than that of AlN-rich (Al₂OC)_1-x(AlN)_x. When temperatures are above 1700°C, the relative content of AlN-rich (Al₂OC)_1-x(AlN)_x is more than that of Al₂OC-rich (Al₂OC)_1-x(AlN)_x. The core-shell structure of aluminum fully ruptures at about 1200°C. Zr₂Al₃C₄ begins to form at about 1000°C and generates in large at 1200°C.     

2.3–21 GHz broadband and high linearity distributed low noise amplifier

This paper focuses on the design of a 2.3–21 GHz Distributed Low Noise Amplifier (LNA) with low noise figure (NF), high gain (S₂₁), and high linearity (IIP3) for broadband applications. This distributed amplifier (DA) includes S/C/X/Ku/K-band, which makes it very suitable for heterodyne receivers. The proposed DA uses a 0.18 μm GaAs pHEMT process (OMMIC ED02AH) in cascade architecture with lines adaptation and equalization of phase velocity techniques, to absorb their parasitic capacitances into the gate and drain transmission lines in order to achieve wide bandwidth and to enhance gain and linearity. The proposed broadband DA achieved an excellent gain in the flatness of 13.5 ± 0.2 dB, a low noise figure of 3.44 ± 1.12 dB, and a small group delay variation of ±19.721 ps over the range of 2.3–21 GHz. The input and output reflection coefficients S₁₁ and S₂₂ are less than −10 dB. The input compression point (P_1dB) and input third-order intercept point (IIP3) are −1.5 dBm and 11.5 dBm, respectively at 13 GHz. The dissipated power is 282 mW and the core layout size is 2.2 × 0.8 mm².     

Investigation on thermal conductivity and mechanical properties of Si3N4 ceramics via one-step sintering

High thermal conductivity Si₃N₄ ceramics were fabricated using a one-step method consisting of reaction-bonded Si₃N₄ (RBSN) and post-sintering. The influence of Si content on nitridation rate, β/(α+β) phase rate, thermal conductivity and mechanical properties was investigated in this work. It is of special interest to note that the thermal conductivity showed a tendency to increase first and then decrease with increasing Si content. This experimental result shows that the optimal thermal conductivity and fracture toughness were obtained to be 66 W (m K)^-1 and 12.0 MPa m^1/2, respectively. As a comparison, the nitridation rate and β/(α+β) phase rate in a static pressure nitriding system, i.e., 97% (MS10), 97% (MS15), 97% (MS20) and 8.3% (MS10), 8.3% (MS15), 8.9% (MS20), respectively, have obvious advantages over those in a flowing nitriding system, i.e., 91% (MS10), 91% (MS15), 93% (MS20) and 3.1% (MS10), 3.3% (MS15), 3.3% (MS20), respectively. Moreover, high lattice integrity of the β-Si₃N₄ phase was observed, which can effectively confine O atoms into the β-Si₃N₄ lattice using MgO as a sintering additive. This result indicates that one-step sintering can provide a new route to prepare Si₃N₄ ceramics with a good combination of thermal conductivity and mechanical properties.